Method and apparatus using a split case die to press a part and the part produced therefrom

ABSTRACT

A split case die is used to press powder, wherein the die parts are moveable in a direction non-parallel to the direction of the pressing axis. The part produced by such a split case die has an external surface with parting line marks oriented in a direction non-perpendicular to the pressing axis.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a divisional of U.S. application Ser. No. 11/945,647 filed Nov. 27, 2007.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The invention is directed to a metallurgical process for the consolidation of powder, wherein the process involves the utilization of a split case die. The subject invention is also directed to a part produced from such a process.

2. Description of Related Art

Fabrication of cutting inserts from sinterable powder, i.e. metallurgical cermets or ceramic powders, involves compaction of the sinterable powder with or without a fugitive binder into a pre-sintered part. Subsequent sintering of the part produces a finished part which may be a cutting tool. Compaction takes place under high pressure obtained through large opposing forces generated by top and bottom rams urged into a die cavity formed in a die containing the sinterable powder.

U.S. Pat. No. 6,986,866 is directed to a method and apparatus for cross-hole pressing to produce cutting inserts, whereby a solid unified die having a die cavity within is utilized to produce a part. The part is ejected through the unified die cavity and, as a result, the shape of the part is limited to a shape able to “slide” through and out of the die cavity.

United States Patent Application Publication No. US 2006/0165828 is directed to a method and apparatus for manufacturing a cutting insert, whereby a split case die is separable in a direction parallel to the pressing axis to produce a part that would not be able to freely pass through the die cavity on either side of the part. However, utilizing such an arrangement, the features on the side of the part must be configured such that the die parts may slide over them to release the part. Not only does this requirement dictate limitations on the shape of the part but, furthermore, the die parts sliding over the part introduce friction against the part that might damage the part.

A process and apparatus is needed for use in a pressing operation, whereby the shape of the part is not subjected to release from the die by sliding through the die or by having die parts slide over the part.

SUMMARY OF THE INVENTION

In one embodiment, a cutting insert is comprised of a sintered green part having a top surface and a bottom surface with side walls therebetween. At least two opposing side walls are symmetric about a longitudinal axis and the at least two opposing side walls each have restrictions extending therein. The part further includes parting line marks extending from the top surface to the bottom surface, wherein the parting line marks are from split case die segments during a powder pressing operation used to fabricate the insert.

Another embodiment is directed to a method for making a part from powder using a uniaxial press comprises the steps of: a) with a die having at least two separable die parts that in the assembled state define a die cavity with a die chamber therein and a pressing bore along a pressing axis extending from opposing sides of the chamber through the die outer surface, positioning the die parts together in the assembled state; b) filling the die and the pressing bores with powder; c) using at least one top ram and at least one bottom ram movable relative to one another along the pressing axis proximate to the chamber; compressing the powder to within the region of the chamber; and d) with each separable die part having a chamber part which together defines the die chamber, spacing apart the top and bottom rams from each other and separating the die parts in a direction non-parallel to the pressing axis to release the part.

Yet another embodiment is directed to an article formed using the method just described.

Yet another embodiment is directed to an article comprised of compacted powder, wherein the article has a body with a primary axis extending therethrough. The body is formed through a pressing operation and the external surface of the body has parting line marks representing mating lines of split case die parts assembled to form a die chamber for forming the part in a direction non-perpendicular to the pressing axis.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a perspective view of a part representing a cutting insert for use in metalworking operations;

FIG. 2 illustrates a side view of the part illustrated in FIG. 1;

FIG. 3 is a schematic of a split case die with top and bottom rams which act in concert with the split case die;

FIG. 4 is a schematic of the same elements in FIG. 3 but repositioned to show a “fill” configuration;

FIG. 5 is a schematic with the same parts as FIG. 3 but in a configuration illustrating compression of a part;

FIG. 6 is a schematic with parts similar to those in FIG. 3 but illustrating the top and bottom rams slightly removed from the part to provide for decompression;

FIG. 7 is a schematic of the parts illustrated in FIG. 3 but with the die parts moving away to illustrate separation;

FIG. 8 is a schematic of the die parts illustrated in FIG. 3 but configured to eject the compressed part;

FIGS. 9 and 10 illustrate one split case die in the assembled state and in the separated state, respectively, in accordance with the subject invention;

FIG. 11 illustrates the detail of a single die part from the die of FIGS. 9 and 10;

FIG. 12 illustrates a perspective view of a base plate upon which die parts of a different die are mounted, wherein the die parts are in the open position;

FIG. 13 illustrates the perspective view similar to that illustrated in FIG. 12 but with the die parts in the closed position;

FIGS. 14A and 14B illustrate a schematic section view of the die in FIGS. 12 and 13 in the separated position and in the assembled position, respectively.

FIG. 15 illustrates a perspective view of the underside of a base plate;

FIGS. 16A, 16B, and 16C illustrate a schematic of the top view of the base plate showing different paths the die parts may travel;

FIG. 17 illustrates die parts in a separated state subsequent to fabricating a complex part;

FIG. 18 is an enlarged view of the part shown in FIG. 18;

FIG. 19 illustrates the die parts in the assembled position to fabricate the complex part shown in FIGS. 17 and 18;

FIGS. 20A, 20B, 20C, and 20D illustrate different internal die chamber shapes to determine when the use of a split case die is most beneficial; and

FIGS. 21A, 21B, and 21C illustrate different arrangements, whereby a core pin may be used in conjunction with a split case die.

DETAILED DESCRIPTION OF THE INVENTION

FIGS. 1 and 2 illustrate a part 10 that, after sintering, will be a cutting insert. However, this part 10 will be discussed as it applies to a split case die. FIG. 3 illustrates an arrangement showing a die 60 having the die chamber 50 with a shape generally similar to that of the side view of part 10 illustrated in FIG. 2. In particular, the part 10 has a top surface 12 and a bottom surface 14 with side walls 16, 18, 20, and 22 therebetween. Side wall 16 has a generally vertical segment 17A extending from the top surface 12 and an angled segment 17B extending to the bottom surface 14. Additionally, side wall 20 has a generally vertical segment 21A extending from the bottom surface 14 and an angled segment 21B extending to the top surface 12. The part 10 is symmetric about a centerline 24. It should be noted that the angled segments 17B, 21B of the side walls 16, 20 both overlap the centerline 24. The part 10 has an edge 26 and a diametrically opposing edge 28 that, after sintering, will be utilized as cutting edges.

Attention will now be directed to FIG. 3 showing the die 60 for use with a uni-axial press for forming a compressed part 10 (FIG. 2) from powder. As a brief overview, the die 60 has a die cavity 65 made up of a die chamber 50 in which the compressed part 10 (FIG. 2) is formed. A first pressing bore 68 is in the die cavity 65 on one side of the die chamber 50, while a second pressing bore 70 is in the die cavity 65 on the opposite side of the die chamber 50. A top ram 72 is moveable within the first pressing bore 68 along arrow 71A, while a bottom ram 74 is moveable within the second pressing bore 70 along arrow 71B. Each ram is moveable to a compressed position to the edge 52, 54 of the die chamber 50. With the top ram 72 and the bottom ram 74 extended into the respective pressing bores 68, 70, the die chamber 50 has a configuration essentially identical to the configuration of the part 10.

It should be noted, however, with respect to FIG. 3, that once the part 10 is formed within the die chamber 50, it is essentially captured within the die chamber 50 and cannot be removed intact without separating the die 60, even with the top ram 72 and the bottom ram 74 fully withdrawn. However, in accordance with the subject invention, the die 60 is a split case die such that, for example, die part 61 is separate and distinct from die part 62. The die parts 61, 62 are separated for purposes of this explanation along a parting line 75 aligned with the pressing axis 77. As a result, as illustrated in FIG. 7, the die part 61 may be separated from the die part 62 along, for example, the direction of arrows 58A, 58B, to provide sufficient clearance for the part 10 to be easily removed from the die 60.

While parting line 75 is illustrated as a straight line, the line may also have a non-straight configuration, depending upon the shape of the desired part and the desire to separate the die parts without interference.

FIGS. 3-8 will now be discussed with attention directed to the method for making the part 10 from powder using a uni-axial press.

The die 60 has at least two separable die parts 61, 62 that, in the assembled state (FIG. 3), define the die cavity 65 with the die chamber 50 therein. The first pressing bore 68 extends along the pressing axis 77 from the die chamber 50 through the die upper outer surface 80. The second pressing bore 70 extends along the pressing axis 77 from the die chamber 50 through the die lower outer surface 82. FIG. 3 illustrates the die part 61, 62 together in the assembled state. As illustrated in FIG. 4, the bottom ram 74 is moved upwardly to occupy a portion of the second pressing bore 70. Thereafter, the die cavity 65 is filled with the appropriate amount of powder 85, such that, when the top ram 72 and the bottom ram 74 are brought toward one another to the edges 52, 54 of the die chamber 50, powder 85 is compressed into a configuration of the final part 10 (FIG. 1).

It should be appreciated that the top ram 72 and the bottom ram 74 are moveable relative to one another along the pressing axis 77 proximate to the die chamber 50 and compress the powder 85 to the volume of the die chamber 50. It is possible to retain the bottom ram 74 in a fixed position and, to move the die 60 and the top ram 72 downwardly to produce the fully compressed part 10.

FIG. 5 illustrates the top ram 72 and the bottom ram 74 in their fully compressed position, thereby defining the part 10.

Although after the part 10 is sintered and the resulting part is essentially rigid, prior to sintering the part 10 the compressed powder does have some resiliency. As a result, when the steps for removing the part 10 from the die 60 are initiated, the highly compressed part 10 resiliently expands to a neutral state. If this decompression were permitted to occur in an unencumbered fashion, the part 10 might become stressed and cracked. As a result, the top ram 72 and the bottom ram 74, after the part 10 is fully compressed (FIG. 5), are moved slightly apart, as illustrated in FIG. 6, to permit the part 10 to decompress but only to a predetermined amount, as illustrated by the top gap 87 associated with the top ram 72 and the bottom gap 90 associated with the bottom ram 74. These gaps 87, 90 provide partial volume relief to the part 10, thereby permitting controlled decompression. The part 10 expands to generally fill these newly generated gaps 87, 90. Thereafter, as illustrated in FIG. 7, the die parts 61, 62 are separated laterally from one another to provide sufficient clearance for the part 10 to be removed from what was the die cavity 65. It should be noted that, as illustrated in FIG. 7, the die part 61 moves relative to the die part 62 in a direction non-parallel to the pressing axis 77 to release the part 10. As illustrated in FIG. 8, the die parts 61, 62 displaced a sufficient amount relative to the part 10, such that the part 10 is free from the die 60 and may be thereafter removed.

As illustrated in FIG. 5, the die parts 61, 62 are assembled together, to create a die chamber 50 which captures the part 10 so that it is immovable within the die cavity 65.

What has so far been described is the method of compressing powder 85 to provide a compressed part 10. However, the manner by which the die parts 61, 62 (FIG. 6) are compressed and assembled will now be illustrated. FIGS. 9-11 illustrate a circular die 60 made up of a first die part 61, second die part 62, third die part 63, and fourth die part 64. For purposes of this discussion, each die part is identical and is comprised of a 90 degree portion of the cylindrical die 60. However, as will be discussed, one or more die parts may also be different to accommodate the desired shape of a part. A top ram (not shown) and a bottom ram (not shown) travel within the die cavity 65 along the pressing axis 77. The die 60 has a top outer surface 80 and a bottom outer surface 82 and the die cavity 65 extends therethrough along the pressing axis 77. The cavity 65 is made up of a die chamber 50 having walls with edges 52, 54 defining the shape of a part 10 in the compressed state. The die cavity 65 also has a first pressing bore 68 extending from one edge 52 of the die chamber 50 to the upper outer surface 80 and a second pressing bore 70 extending from one edge 44 of the die chamber 50 through the lower outer surface 82. Directing attention to FIG. 10, each of the die parts 61, 62, 63, 64 has a pair of parting surfaces 61A, 61B, 62A, 62B, 63A, 63B, 64A, 64B. The parting surfaces of adjacent die parts abut against one another to form the assembled cylindrical die 60 illustrated in FIG. 9. It should be noted that the parting surfaces are not perpendicular to the pressing axis 77 so that the die parts 61, 62, 63, 64 may move apart in a direction other than parallel to the pressing axis 77, thereby avoiding damage to the part 10 when the shape of the part 10 is such that the die parts 61, 62, 63, 64 could not be released with motion along the pressing axis 77. As a result, the die parts 61, 62, 63, 64 must move in a direction non-perpendicular to the pressing axis 77 to release the part 10. Such a motion provides great flexibility in pressing a desired shape into a part 10 and releasing the part 10 from the die without sliding the die against the part 10 or damaging any overhanging or under hanging projection on the part 10 that would result if the part 10 was ejected along the pressing axis 77.

Each die part 61, 62, 63, 64 has a die chamber portion with opposing pressing bore portions. As an example, directing attention to die portion 62, which is representative of the other die portions 61, 63, 64, a die chamber portion 50A is surrounded by a first pressing bore portion 68A and a second pressing bore portion 70A. The chamber portions 50A, 50B, 50C, 50D together define the die chamber 50.

Although, for illustrative purposes, FIGS. 9-11 have illustrated four die parts 61, 62, 63, 64 essentially identical in shape with identical cavity portions 50A, it should be appreciated that, depending upon the desired configuration of the part 10, there may be two or more die parts and the pressing bore portions and the cavity parts of each die portion may be substantially different to accommodate not only the shape of the part 10 but, furthermore, to provide for the most efficient manner of loading the die cavity with powder and, furthermore, for releasing the part 10 from the die.

FIGS. 9-11 have been presented to show the operation of the die parts 61, 62, 63, 64 and it should be appreciated that the cavity 50 and first pressing bore 68 and the second pressing bore 70 have been drawn in schematic only to illustrate their operation. The shape of the die cavity 50, the first pressing bore 68, and second pressing bore 70 may be any number of different geometries intended to accommodate the shape of the part 10 intended to be produced. Also, while the die parts 61, 62, 63, 64 have been illustrated as four identical pieces of a cylinder, depending upon the desired shape of the part 10, there may be as few as two die parts and each die part may have a completely different configuration limited only by the fact that the die parts must be able to move apart freely to release the compressed part.

Although the die parts 61, 62, 63, 64 fit together closely, as a result of manufacturing tolerances, when the part 10 is compressed, there will be parting line marks imparted to the external surface of the part 10. FIGS. 5-8 show such a parting line mark 30. While this mark 30 is shown as straight, the contour of this mark 30 is dependent upon the mating pattern of the die parts. Additionally, depending upon the manufacturing tolerances, the parting line mark may not be easily visible with the naked eye. Additionally, the parting line mark 30 extends around the entire part 10. However, when the parting line mark 30 is located along a corner or an edge of the part 10, it may be difficult to discern.

So far, schematics have been used to describe the subject invention. FIGS. 12-14 illustrate actual hardware used to achieve one embodiment of the method and apparatus. For purposes of distinction, similar parts of the apparatus will be incremented by 100 from the reference numbers used to discuss the previous figures

FIGS. 12-14 illustrate a uni-axial press 200 without the top and bottom rams illustrated. The uni-axial press 200 is used for forming a part (not shown) from compressed powder. The press 200 is comprised of a base 205 having a floor 210 used to support a die 160 made up of die parts 161, 162, 163, 164, which are shown in their separated state in FIG. 12, and shown in their assembled state in FIG. 13. The method for producing a part 10 is the same as that method previously discussed using the schematic figures; however, as can be seen in FIGS. 12 and 13, the die cavity 165 has a substantially different shape for the purposes of producing a differently shaped part.

Nevertheless, the die parts 161, 162, 163, 164 are secured to the base 205 but are also permitted to slide upon the base 205 between the separated state (FIG. 12) and the assembled state (FIG. 13).

Directing attention to FIG. 12, the die parts 161, 162, 163, 164 are biased to the separated position. In particular, each die part 161, 162, 163, 164 has associated with it a spring mechanism 215 and, for purposes of discussion, the spring mechanism 215 associated with die part 161 will be discussed with the understanding that this spring mechanism and its operation is identical for the remaining die parts 162, 163, 164.

The first end 217 of a cable 218 is attached to the die part 161, while a second end 219 of the cable 218 is connected to a tensioning bolt 220 slidably secured within a bracket 222. The bracket 222 is firmly secured to the base 205 using fasteners 225, such as bolts. The bolt 220 is biased by a compression spring 227 to maintain the cable 218 in tension. In particular, the bolt 220 has a bolt head 221 that is engaged by the compression spring 227, whereby, as seen in FIG. 12, the bolt 220 is urged to the right. The cable 218 extends radially from the die part 161 and wraps around a pivot pin 229. The second end 219 of the cable 218 is attached to the tensioning bolt 220. The spring mechanism 215 associated with each die part 161, 162, 163, 164 acts to bias each die part to the separated position. While the spring mechanism 215 has been discussed as one embodiment for separating the die parts, other mechanisms, such as hydraulic cylinders, may also be used.

FIG. 13 illustrates the die parts 161, 162, 163, 164 in the assembled position clearly defining the die cavity 165 and compressing the compression spring 227 by pulling the cable 218 with the die part 161 into the assembled position. As clearly illustrated in FIG. 13, the profile of the side surface 167 of the die 160 is conical, such that the side surface 167 of the die parts 161, 162, 163, 164 in the assembled state forms a die cone 173.

FIG. 14A illustrates the die 160 with the conical side surfaces 167 and, furthermore, illustrates a retainer 270 having an interior surface 272 with a recessed cone 274, wherein the recessed cone 274 has a shape corresponding to the die cone 173, such that the retainer 270 captures the conical die parts 161, 162, 163, 164 and secures them together in the assembled state as illustrated in FIG. 14B, and as illustrated without the retainer 270 in FIG. 13.

FIG. 14B illustrates a cone angle X between the centerline 275 of the die 160 and the side surfaces 167 of the die cone 173 and between the centerline 275 of the die 160 and the interior surface 272 of the recessed cone 274 of the retainer 270. The cone angle X between each of the die cone 273 and the recessed cone 274 may form a Morse taper, which is a low angle taper which results in a self-sticking friction connection between the die cone 173 and the recessed cone 274. The cone angle X, for each of the die cone 173 and the recessed cone 274, may be between 10 and 20 degrees.

In order to move the retainer 270 down over the die 160 to position the die 160 from the separated state to the assembled state, the recessed cone 274 is placed over the die cone 173, such that the interior surface 272 of the recessed cone 274 urges the side surfaces 167 of the die cone 173 radially inwardly. To achieve this, it is necessary for the retainer 270 to be moved against the die cone 173 with a force sufficient to overcome the bias of the spring mechanism 215 (FIG. 12) associated with each of the die parts 161, 162, 163, 164. A drive mechanism (not shown) displaces the retainer 270 to position the die parts 161, 162, 163, 164 from the separated position to the assembled position. The drive mechanism may be one or more hydraulic cylinders (not shown).

FIG. 14A shows the retainer 270 spaced a significant vertical distance from the die 160. In actuality, however, the separation of the die parts 161, 162, 163, 164 need only be a sufficient amount to permit the part (not shown) to be released from the die cavity 165. Any greater separation is unnecessary and may be undesirable. Therefore, in order to control the degree of separation of the die parts 161, 162, 163, 164, the vertical motion of the retainer 270 is closely controlled. In particular, and with respect to FIG. 14B, restrictor bolts 280 extend through bores 282 through the retainer 270. The restrictor bolts 280 extend into a foundation plate 284 which may be the base 205 (FIG. 13). Nuts 286 may be secured to the ends of the restrictor bolts 282 to restrict the bolt motion relative to the foundation plate 284. However, the restrictor bolts 280 are elongated and have a bolt head 281 slightly spaced from the top surface 289 of the retainer 270. As a result, as the retainer 270 is moved upwardly, the spring biased die parts 161, 162, 163, 164 (FIG. 13) are urged radially outwardly but only the amount permitted by the vertical motion of the retainer 270, which itself is limited by the gap g between the top surface 289 of the retainer 270 and the bottom surface 288 of each bolt head 281. Spacers 295 may be placed between the nuts 286 and the foundation plate 284 to limit the degree to which the retainer 270 may move and, as a result, to limit the degree to which the die parts 161, 162, 163, 164 may move laterally to a separated state.

When the die parts 161, 162, 163, 164 are assembled to form the die chamber 150, the die parts will mate and form parting lines on the wall of the die chamber 150. These parting lines produce a groove in the die chamber 150. The groove produced by these parting lines will be imparted to the part as parting line marks and, depending upon the precision with which the die parts 161, 162, 163, 164 mate in the region of the die chamber 150, these parting line marks will be more prominent or less prominent. However, they will always exist to some degree.

The green part 10 illustrated in FIG. 1 may be fabricated utilizing the uni-axial press 200 with the die cavity 165 illustrated in FIGS. 12 and 13. As seen in FIGS. 12 and 13, the die parts 161, 162, 163, 164 move back and forth from the separated position to the assembled position along a radial path, for example, path 287 associated with die part 161 illustrated in FIG. 12. Die part 161, just as the remaining die parts 162, 163, 164, moves within the radial path 287 (FIG. 12) along a bearing 285 defined by a guide slot 290 (FIG. 12) extending within the base 205 of the uni-axial press 200. As illustrated in FIG. 12, the guide slot 290 is oriented radial to the pressing axis 277 through the base 205, just as the remaining guide slots 291, 292, 293 are radial to the pressing axis 277 to guide die parts 162, 163, 164, respectively.

It should be noted that the base 205 is a stand-alone part having guide pins 294A, 294B, 294C, 294D that fit within predefined bores within the uni-axial press 200. The base 205 is interchangeable with other bases that may contain other dies so that the same uni-axial press 200, depending upon the base mounted upon that uni-axial press 200, may be used to fabricate different parts for a variety of different cutting tools.

FIG. 15 illustrates the bottom of the base 205 with evacuation slots 296A, 296B, 296C, 296D through which residual powder may fall to keep the base 205, the spring mechanism 215, the bearings 285, and the external surfaces of the die parts 161, 162, 163, 164 free of excess powder that may detract from the proper opening and closing of the die parts 161, 162, 163, 164.

A primary goal in the design of the path a particular die part follows, from the assembled state to the separated state, is to separate the die part from the part after compression in a manner that does not disturb the part. In particular, using the split case die in accordance with the subject invention, a multitude of shapes may be imparted to a part, even shapes with undercuts and an appropriate die part configuration for that die part may be established to eliminate interference between the die part and the part during separation. A term of art used to describe this interference is backdraft.

FIGS. 16A, 16B, 16C illustrate different paths that a die part might follow when being separated from a part to avoid backdraft. In particular, with respect to FIG. 16A, guide slots 297A, 297B, 297C, 297D are positioned to define an offset radial straight path. These configurations would be imparted to the guide slots 290, 291, 292, 293, illustrated in FIG. 15, for a particular base.

Directing attention to FIG. 16B, guide slots 298A, 298B, 298C, 298D illustrate a non-linear curved path that the die parts might follow to release a part. Finally, directing attention to FIG. 16C, it is not necessary for the path of one guide slot, such as 299A, to resemble that path for another guide slot, such as 299B. FIG. 16C illustrates the variety of different paths with guide slots 299A, 299B, 299C, 299D that may be selected to release a die portion from a part without imparting backdraft to the part.

The split case die in accordance with the subject invention, comprises die parts which move in a direction different than that from the pressing axis and, by doing so, allows a part to be shaped into geometries not previously available through a pressing operation. In the past, injection molding techniques were utilized or pressing techniques were utilized where, after the initial pressing operation, the part required extensive grinding to arrive at the final shape. Through the split case die used with the uni-axial press described herein, part shapes not previously available by a pressing operation may now be produced.

What has so far been described is the hardware associated with the fabrication of the part 10 illustrated in FIGS. 1 and 2, utilizing the split case die uni-axial press in accordance with the subject invention.

It is possible with such a split case die to fabricate parts having complex surfaces on any side. Directing attention to FIGS. 17 and 18, a die 360 is comprised of die parts 361, 362, 363, 364, which, in the instance illustrated in FIGS. 17 and 18, are moveable in a direction radial to the pressing axis 377. A top ram 372 represented only by the end of the top ram and a bottom ram 374 move relative to one another along the pressing axis 377. In the assembled state (FIG. 20), the die parts 361, 362, 363, 364, the top ram 372, and the bottom ram 374 define the die chamber 350 which has a shape identical to the part 310 formed during the pressing operation. Green part 310, better illustrated in FIG. 18, is made up of a top surface 312, a bottom surface 314, and side walls 316, 318, 320, 322 therebetween. A typical side wall 322 is comprised of a pair of primary cutting edges 380A, 384A and secondary cutting edges 382A, 386A adjacent thereto. For this particular part 310, each side has such a cutting edge arrangement and, as a result, the primary cutting edge 380B and secondary cutting edge 382B, associated with side wall 316, provide a projection 388 extending from a recessed plateau or seating pad 390, which is the innermost portion of side wall 322. Diametrically opposed to projection 388 is another projection 392 associated with cutting edges on the opposite side of the part 310. This combination of recessed surfaces and projections provides a geometry that is ideally suited for the split case die uni-axial press in accordance with the subject invention. In particular, returning to FIG. 17 and directing attention to die part 364, the face 395 of the die part 364 has a contour essentially identical to the contour of the side wall 322. For purposes of explaining, the die face 396 associated with die part 363 will be utilized with the understanding that these two faces 395, 396 are identical.

For purposes of explanation, die face 396 (FIG. 17) will be discussed in conjunction with side wall 322 (FIG. 18) of the part 310. For at least part 310, all four sides are identical and the view of side 322 is more revealing than the view of side 320. The die face 396 (FIG. 17) has a seating pad projection 399 used to form the seating pad 390 (FIG. 18) and has additional surfaces that are reflected from examination of the side wall 322. FIG. 20 illustrates the part 310 with the side walls 316, 322 within the die chamber 350 to form the part 310. The face 395 of die part 364 and the face 398 of die part 361 define the contour of the side wall 322, 316 of the part 310. It can be appreciated, with respect to FIG. 19, that the part 310 is immovable along pressing axis 377 within the die chamber 350, even with the top ram 372 and bottom ram 374 removed because it is captured by the die parts 361, 362, 363, 364 (FIG. 17) and may only be released by a motion of each die part 361, 362, 363, 364 that is nonparallel to the pressing axis 377. The part 310 would not tolerate any relative motion that is entirely parallel to pressing axis 377. FIG. 17 illustrates the direction of the displacement required to release the part during this pressing operation.

Depending upon the geometry of the die chamber, a split case die may be required to press a certain part. Directing attention to FIG. 20A, a die chamber 450 having an open end 452 with no restrictions would not require a split case die because the part may be urged in the direction of arrow 454 along the pressing axis 477 to eject the part 410 from the die 460. FIG. 20B, although relatively simple, illustrates a configuration ideal for a split case die pressing operation. The wall 553 of the die chamber 550 has at least one portion 554 that forms a positive angle Y with the pressing axis 577 and at least one other portion 555 that forms a negative angle Z with the pressing axis 577. The combination of surfaces with these angles defines a part that is captured by the die chamber 550 and cannot be safely removed from the die chamber 550 without laterally displacing the die parts of the split case die.

While the arrangement illustrated in FIG. 20B is a fairly simple configuration, the features illustrated may be applied to much more complex arrangements suitable for fabrication using a split case die pressing operation.

In FIG. 20B, die chamber 550 includes a restriction 552 that would prevent the part 510 from being axially displaced along the pressing axis 577 to displace the part 510. Therefore, a die having a die chamber 550 is ideal for the split case die in accordance with the subject invention.

Directing attention to FIG. 20C, the die chamber 650 includes a bellow-shaped wall 652 that captures the part 610 and does not permit movement of the part along the pressing axis 677. FIG. 20C illustrates another configuration ideal for a split case die pressing operation. The wall 662 of the die chamber 650 has a concave surface 663 along a plane non-perpendicular to the pressing axis 677. At least one point 665 along the surface 663 between the ends 666, 668 of the surface 663 have a tangent parallel to the pressing axis 677.

In the alternative, the wall 662 of the die chamber 650 may have a convex surface 683 along a plane non-perpendicular to the pressing axis 677. At least one point 685 along the surface 683 between the ends 686, 688 of the surface 663 have a tangent parallel to the pressing axis 677.

FIG. 20D illustrates yet another die chamber 750 which is capable of imparting to the part 710 a spiral flute 712. This arrangement also is ideally suited for the split case die in accordance with the subject invention.

What has so far been discussed is the fabrication of a part having unique surface features which are most efficiently formed utilizing a uni-axial press and a split case die as described herein.

U.S. Pat. No. 6,986,866 assigned to the Assignee of the present application, entitled “Method and Apparatus for Cross-Hole Pressing To Produce Cutting Inserts” is hereby incorporated by reference and describes a method and apparatus for imparting to a part a cross-hole extending through the part in a direction nonparallel to the pressing axis. However, this patent describes the use of a solid unified die for producing such a cross-hole.

In another embodiment of the subject invention, a cross-hole may be imparted to a part in conjunction with the use of a split case die to provide not only the unique surface features available using a split case die but, furthermore, to provide a hole extending through the part along an axis different from the pressing axis.

FIG. 21A illustrates a die 860 having a die part 861 and an opposing die part 862. A bore 890 extending through the die parts 861, 862 is suitable to accept a cross pin 892 within the die part 861 and a cross pin 893 within the die part 862. In the assembled state, these cross pins 892, 893 contact each other within the die chamber 850, such that when the die parts 861, 862 are assembled and the cross pins 892, 893 are contacting one another, the die cavity 860 may be filled with powder and, upon pressing, the part (not shown) will have a bore extending therethrough in a direction nonparallel to the pressing axis 877, which, as illustrated in FIG. 21A, is into the page. In the arrangement illustrated in FIG. 21A, the die part 861 and the die part 862 are moveable along arrows 894, 895, which is the same direction the cross pins 892, 893 move. Note the cross pins 892, 893 are not limited to motion parallel with the die parts 861, 862.

Directing attention to FIG. 21B, die parts 961, 962, 963, 964 of die 960 are moveable in a radial direction indicated by arrows 994, 995, 996, 997 which extend radially from the pressing axis 977 which is into the page. Cross pins 992, 993 may be positioned within indentations 970, 971, 972, 973 found in die parts 970, 971, 972, 973, respectively, which would accommodate cross pins 992, 993 when the die 960 is in the assembled state. The cross pins 992, 993 contact within the die chamber 950. Thereafter, when the die chamber 950 is filled with powder and that powder is compressed to form a part, the part will have the cross bore imparted by the cross pins 992, 993. It should be noted that in FIG. 21B the cross pins 992, 993 move in a direction along arrows 998 and 999, which is different than the direction of the die parts specified by arrows 994, 995, 996, 997.

Directing attention to FIG. 21C, unlike FIG. 21B, where indentations 970, 971, 972, 973 were placed within the wall of each die part 961, 962, 963, 964, die 1060 is comprised of die parts 1061, 1062, 1063, 1064 moveable along arrows 1094, 1095, 1096, 1097. However, the cross pins 1092, 1093 which move together to mate within the die chamber 1050 radial to the pressing axis 1077, which is into the page, extend through bores 1080, 1082 within die part 1063, 1064 in a direction along arrows 1098, 1099 different from the direction specified by arrows 1094, 1095, 1096, 1097. Once again, in the assembled state, the die chamber 1050 is filled with powder and compressed such that the part has a bore extending therethrough along an axis different from the pressing axis 1077.

While specific embodiments of the invention have been described in detail, it will be appreciated by those skilled in the art that various modifications and alternatives to those details could be developed in light of the overall teachings of the disclosure. The presently preferred embodiments described herein are meant to be illustrative only and not limiting as to the scope of the invention which is to be given the full breadth of the appended claims and any and all equivalents thereof. 

1. A cutting insert comprised of a sintered green part having a top surface and a bottom surface with side walls therebetween and, wherein at least two opposing side walls are symmetric about a longitudinal axis and, wherein the at least two opposing side walls each have restrictions extending therein, wherein the part further includes parting line marks extending from the top surface to the bottom surface, wherein the parting line marks are from die segments during a powder pressing operation used to fabricate the insert.
 2. The cutting insert according to claim 1, wherein the restrictions formed in the at least two opposing side walls are comprised of segments with two angled portions, wherein a first angled portion forms a positive angle Y with the longitudinal axis and a second angled portion forms a negative angle Z, which together define a restriction within each of the at least two side walls.
 3. The cutting insert according to claim 2, wherein a spacer portion exists between the two angled portions.
 4. The cutting insert according to claim 3, wherein the spacer portion is straight.
 5. The cutting insert according to claim 4, wherein the spacer portion is parallel to the longitudinal axis.
 6. The cutting insert according to claim 1, wherein restrictions formed in the at least two opposing side walls have a concave surface.
 7. The cutting insert according to claim 6, wherein the concave surfaces are curved.
 8. The cutting insert according to claim 7, wherein the concave surfaces have at least one point between the ends of each concave surface that is tangent to the longitudinal axis.
 9. The cutting insert according to claim 1, wherein the restrictions formed in the at least two opposing side walls make up part of a bellows shape, wherein the restriction is located at an inner section along the bellows.
 10. The cutting insert according to claim 9, wherein the bellows is comprised of adjacent convex and concave sections.
 11. The cutting insert according to claim 1, wherein the restrictions formed in the at least two opposing side walls are comprised of threads on the walls extending around the perimeter of the insert exterior in the form of a spiral flute.
 12. A method for making a part from powder using a uni-axial press, wherein the method comprises the steps of: a) with a die having at least two separable die parts that, in the assembled state, define a die cavity with a die chamber therein and a pressing bore along a pressing axis extending from opposing sides of the chamber through the die outer surface, positioning the die parts together in the assembled state; b) filling the die and the pressing bores with powder; c) using at least one top ram and at least one bottom ram movable relative to one another along the pressing axis proximate to the chamber; compressing the powder to within the region of the chamber; and d) with each separable die part having a chamber part which together defines the die chamber, spacing apart the top and bottom rams from each other and separating the die parts in a direction non-parallel to the pressing axis to release the part.
 13. The method of making a part according to claim 12, wherein after the powder is compressed and before the part is released, compression on the part is relieved to provide partial volume relief to the part.
 14. The method of making a part according to claim 13, wherein the partial volume relief to the part is provided by spacing apart by a small amount the top and bottom rams to decompress the part prior to release of the part.
 15. The method according to claim 12, wherein the die moves in a direction that is radial to the pressing axis.
 16. The method according to claim 12, wherein the die moves in a direction that is offset from the pressing axis.
 17. The method according to claim 12, wherein the die moves in a direction that is linear.
 18. The method according to claim 11, wherein the die moves in a direction that is non-linear.
 19. The method according to claim 12, wherein the assembled die captures the part so that it is immovable within the die cavity.
 20. The method according to claim 19, further including the step of urging the die parts apart after the part has been formed to release the part.
 21. The method according to claim 12, further comprising the step, prior to the step of filling the die chamber, of placing within the uni-axial press any particular base plate with a particular die set to permit the fabrication of different parts using the same uni-axial press.
 22. The method according to claim 12, further comprising the step of inserting a removable core rod within the chamber to define a core bore through the chamber in a direction non-parallel to the pressing axis.
 23. An article formed using a uni-axial press motion having a die with a cavity extending therethrough along a pressing axis, wherein the cavity is made up of a chamber and a pressing bore on each side of the chamber with a top ram and a bottom ram independently movable along the pressing axis within the cavity, wherein the article is formed by the steps of: a) with a die having at least two separable die parts that, in the assembled state, define a die chamber therein and a pressing bore along a pressing axis extending from opposing sides of the chamber through the die outer surface, positioning the die parts together in the assembled state; b) filling the die and the pressing bores with powder; c) using at least one top ram and at least one bottom ram movable relative to one another along the pressing axis proximate to the chamber; compressing the powder to within the region of the chamber; and d) with each separable die part having a chamber part which together defines the die chamber, spacing apart the top and bottom rams from each other and separating the die parts in a direction non-parallel to the pressing axis to release the part.
 24. The article according to claim 23, wherein after the powder is compressed and before the part is released, compression on the part is relieved to provide partial volume relief to the part.
 25. The article according to claim 23, wherein the assembled die captures the part so that it is immovable within the die.
 26. The method according to claim 23, further comprising the step of inserting a removable core rod within the chamber to define a core bore through the chamber at the compression region in a direction perpendicular to the pressing axis.
 27. An article comprised of compacted powder, wherein the article has a body with a primary axis extending therethrough, wherein the body is formed through a pressing operation and, wherein the external surface of the body has parting line marks representing mating lines of split case die parts assembled to form a die chamber for forming the part in a direction non-perpendicular to the pressing axis.
 28. The article according to claim 27, wherein the article is a cutting insert that has been sintered from the part. 